Bloc Multilayers 3D

Multilayer 3D

Layer 1 of 20% at strength +/- 600 Mpa
Layer 2 de 15% at strength+/- 660 Mpa
Layer 3 de 15% at strength de +/- 730 Mpa
Layer 4 de 15% at strength de +/- 780 Mpa
Layer 5 de 15% at strength de +/- 830 Mpa
Layer 6 de 20% at strength de +/- 900 Mpa


Composition :

Y2O3 = 9,28wt%
AI2O3 = 0,05wt%
SiO2 < 0.15wt%
CO3O4 <0.02wt%

Finished :

at 1450°C before 60 mins

Cavex CA37 Fast Set

Features :

- worldwide reference
- firm consistency
- more rigid impression
- good tear and deformation resistance
- detail reproduction at least 50µm
- dust free
- pink peppermint aroma
- compatible with all types of gypsum, smooth gypsum surface
- patient friendly setting times in mouth

Normal Set 1.30 minutes
Fast Set 1 minute

Multilayer 3D

Layer 1 of 20% at strength +/- 600 Mpa
Layer 2 de 15% at strength+/- 660 Mpa
Layer 3 de 15% at strength de +/- 730 Mpa
Layer 4 de 15% at strength de +/- 780 Mpa
Layer 5 de 15% at strength de +/- 830 Mpa
Layer 6 de 20% at strength de +/- 900 Mpa


Composition :

Y2O3 = 9,28wt%
AI2O3 = 0,05wt%
SiO2 < 0.15wt%
CO3O4 <0.02wt%

Finished :

at 1450°C before 60 mins

Multilayer 3D

Layer 1 of 20% at strength +/- 600 Mpa
Layer 2 de 15% at strength+/- 660 Mpa
Layer 3 de 15% at strength de +/- 730 Mpa
Layer 4 de 15% at strength de +/- 780 Mpa
Layer 5 de 15% at strength de +/- 830 Mpa
Layer 6 de 20% at strength de +/- 900 Mpa


Composition :

Y2O3 = 9,28wt%
AI2O3 = 0,05wt%
SiO2 < 0.15wt%
CO3O4 <0.02wt%

Finished :

at 1450°C before 60 mins

Multilayer 3D

Layer 1 of 20% at strength +/- 600 Mpa
Layer 2 de 15% at strength+/- 660 Mpa
Layer 3 de 15% at strength de +/- 730 Mpa
Layer 4 de 15% at strength de +/- 780 Mpa
Layer 5 de 15% at strength de +/- 830 Mpa
Layer 6 de 20% at strength de +/- 900 Mpa


Composition :

Y2O3 = 9,28wt%
AI2O3 = 0,05wt%
SiO2 < 0.15wt%
CO3O4 <0.02wt%

Finished :

at 1450°C before 60 mins